W与Ti_3SiC_2陶瓷的放电等离子烧结连接  

Joining of W and Ti_3SiC_2 ceramic by spark plasma sintering

作　　者：易耀勇 谢珩[2] 倪东惠[3] 郑军君[3] 

机构地区：[1]广东省工业技术研究院焊接技术研究所,广东广州510650 [2]惠州学院,广东惠州516007 [3]华南理工大学 国家金属材料近净成形工程技术研究中心,广东广州510640

出　　处：《焊接技术》2012年第6期5-7,1,共3页Welding Technology

基　　金：国家自然科学基金项目(50774036);广东省自然科学基金项目(8151064101000029)

摘　　要：本研究成功地以放电等离子烧结方法将W和Ti3SiC2块体连接,得到界面结合良好、组织均匀、晶粒细小、没有明显缺陷的界面组织,通过生成以WC和W2C为主的过渡层,连接界面形成了冶金结合,为陶瓷与金属材料的连接提供了一条新途径。W and Ti3SiC2 were successfully joined together by spark plasma sintering technique.A strong binding interface with uniform fine grains and without significant defects was obtained,which paving a new way for joining ceramics and metals.Metallurgical bonding was obtained at the joint interface by forming intermediate layers composed of mostly WC and W2C.

关 键 词：TI3SIC2 W 连接 放电等离子烧结 

分 类 号：TG496[金属学及工艺—焊接]