脉冲电沉积工艺参数对Ni-SiC复合镀层性能的影响  

Effect of pulse electrodeposition parameters on the performance of Ni-SiC composite coatings

作　　者：马春阳[1] 丁俊杰[1] 楚殿庆[2] 

机构地区：[1]东北石油大学机械科学与工程学院,黑龙江大庆163318 [2]大庆油田有限责任公司采油四厂,黑龙江大庆163000

出　　处：《兵器材料科学与工程》2012年第4期65-67,共3页Ordnance Material Science and Engineering

摘　　要：采用脉冲电沉积的方法,在20钢表面制备Ni-SiC复合镀层。利用显微硬度计和摩擦磨损试验机研究工艺参数对Ni-SiC复合镀层性能的影响规律,利用扫描电镜观察Ni-SiC复合镀层的表面形貌。结果表明,SiC粒子浓度、阴极电流密度、占空比等工艺参数对Ni-SiC复合镀层的性能和表面形貌有很大影响。当SiC质量浓度为8 g/L、电流密度为4 A/dm2、占空比为10%时,Ni-SiC复合镀层表面的颗粒相对较小,致密性好,镀层中大量均布着小颗粒的SiC粒子。Ni-SiC composite coatings were prepared on the 20 steel using pulse electrodeposition method. The effect of processing parameters on the performance was investigated using micro-hardness tester and friction and wear tester. The results illuminate that the SiC concentration, current density and duty cycle have great effect on the performance and microstructure of Ni-SiC com- posite coatings. A large number of smaller SiC particles are uniformly distributed on the Ni-SiC composite coatings with good compactness, when the SiC concentration, current density and duty cycle are 8 g/L,4 A/din2, 10%, respectively.

关 键 词：脉冲电沉积 硬度 摩擦磨损 

分 类 号：TG174[金属学及工艺—金属表面处理]