Homogenization of twin-roll cast A8006 alloy  

双辊激冷铸造A8006合金的均匀化(英文)

作　　者：陈忠伟[1] 李士顺[1] 赵静[1] 

机构地区：[1]西北工业大学凝固技术国家重点实验室,西安710072

出　　处：《Transactions of Nonferrous Metals Society of China》2012年第6期1280-1285,共6页中国有色金属学报（英文版）

基　　金：Project (42-QP-009) supported by Research Fund of the State Key Laboratory of Solidification Processing,China;Project (Z2012019) supported by Graduate Starting Seed Fund of Northwestern Polytechnical University,China;Project (B08040) supported by 111 Project

摘　　要：Microstructure and hardness of twin-roll casting （TRC） process and direct-chill casting （DC） for A8006 alloy with and without homogenization were investigated by means of scanning electron microscopy （SEM）, X-ray diffraction analysis and Vickers hardness measurement. The results show that the eutectic phase of the homogenized TRC alloy becomes fine as the microstructure of the as-cast TRC alloy is refined. The short rodlike eutectic phase of the as-cast TRC alloy is dispersed homogeneously, which is similar to the morphology of eutectic phase of the homogenized DC alloy. After homogenization, elements Fe and Mn in DC and TRC alloys are diffused from eutectic phase to A1 matrix, resulting in the decrease of microhardness. The formability of the as-cast TRC alloy is superior to that of the homogenized DC alloy. For TRC A8006 alloy, the homogenizing cycle can be removed from the subsequent processing.通过SEM、XRD与硬度测定研究均匀化过程对双辊激冷铸造(TRC)与直接冷却铸造(DC)A8006合金的微观组织和性能的影响。结果表明,随着TRC合金微观组织的细化,均匀化后合金中的共晶相进一步细化。DC合金均匀化后其共晶相形态相似于TRC合金中的共晶相形态。均匀化后,合金共晶相中的Fe、Mn元素均匀地扩散到铝基体中,引起合金硬度的降低。TRC合金的成形性能优于均匀化的DC合金,所以,对于TRCA8006合金的后续加工过程可省去均匀化过程。

关 键 词：A8006 alloy twin-roll casting HOMOGENIZATION MICROSTRUCTURE 

分 类 号：TG29[金属学及工艺—铸造]