Synthesis,characterization and antibacterial property of Ag/mesoporous CeO_2 nanocomposite material  

Ag/介孔CeO_2纳米复合材料的合成、表征及抗菌性能(英文)

作　　者：陆晓旺[1,2] 钱君超[3] 陈丰[3] 李霞章[1] 陈志刚[4] 

机构地区：[1]常州大学材料科学与工程学院,常州213164 [2]常州市先进金属材料重点实验室,常州213164 [3]江苏大学材料科学与工程学院,镇江212013 [4]苏州科技学院化学与生物工程学院,苏州215011

出　　处：《Transactions of Nonferrous Metals Society of China》2012年第6期1418-1422,共5页中国有色金属学报（英文版）

基　　金：Projects (21071107, 51002016) supported by the National Natural Science Foundation of China;Project (JQ201003) supported by Changzhou University Fund for Young Talent,China

摘　　要：Mesoporous CeO2 with high specific surface area was synthesized using a modified evaporation-induced self-assembly （EISA） method, and a series of different amounts of Ag were loaded to this mesoporous CeO2 by a modified ethylene glycol reduction route. The samples were characterized by powder X-ray diffraction （XRD）, transmission electron microscopy （TEM）, energy-dispersive spectrometry （EDS）, nitrogen adsorption-desorption, Brunauer-Emmett-Teller （BET） and Barrett-Joyner- Halenda （BJH） methods. The mesoporous CeO2 structure with different proportions of silver nanoparticles and its antibacterial activity were adequately studied, confinnin~ that obtained novel materials show a good antibacterial effect.利用改进的溶剂挥发诱导自组装法(EISA)制备高比表面积介孔CeO2,通过改进的乙二醇还原法,在得到的介孔CeO2中负载上不同量的银。采用粉末X射线衍射(XRD)、透射电子显微镜(TEM)、能谱仪(EDS),N2吸附-脱附法方法对产物进行表征。由BJH方程计算得到材料的孔径分布,以BET法计算材料的比表面积。研究负载不同比例银纳米粒子的介孔CeO2的结构及其抗菌活性。实验表明所制备的新材料具有很好的抗菌性能。

关 键 词：CEO2 MESOPOROUS silver nanoparticle antibacterial activity 