表面接枝β成核剂的玻璃纤维/等规聚丙烯复合材料界面晶体形态研究  

Interfacial Crystal Morphology of Glass Fiber Grafted β-nucleating Agent/Isotactic Polypropylene Composites

作　　者：黄章勇[1] 陈妍慧[2] 唐建华[1] 李忠明[2] 

机构地区：[1]四川大学化学工程学院,四川成都610065 [2]四川大学高分子科学与工程学院,四川成都610065

出　　处：《云南化工》2012年第3期6-9,共4页Yunnan Chemical Technology

摘　　要：通过在玻璃纤维表面接枝β成核剂,期望在界面处诱导等规聚丙烯形成β横晶。结果表明,玻璃纤维表面接枝的β成核所形成的网络结构不够完善,只能诱导形成少量的晶核,不足以形成横晶;在熔融混合过程当中添加少量的硬脂酸钙能够在接枝β成核剂的玻纤表面形成一个完善的网络结构,从而有效的诱导形成β横晶。The purpose of this article is to develop β-transcrystallinity induced by glass fiber grafted β-nucleating agent at the interface of glass fiber and isotactic polypropylene （ipp）. It demonstrates that the network formed by β-nucleating agent grafted on the interface of glass fiber is unstable. Only several nuclei are formed, and β-transcrystallinity is not developed. Adding a little calcium stearate can form a stable net- work on the surface of glass fiber grafted p-nucleating agent during the mixed melt process, and can effectively induce the formation of β-transcrystallinity.

关 键 词：等规聚丙烯 玻璃纤维 β横晶 

分 类 号：O632.12[理学—高分子化学]