熔盐钠热还原NbCl_5制备金属铌粉  

Preparation of Niobium Powder by Sodiothermic Reduction of NbCl_5 in Molten Salts

作　　者：王娜[1] 朱鸿民[1] 

机构地区：[1]北京科技大学冶金与生态工程学院,北京100083

出　　处：《有色金属（冶炼部分）》2012年第7期44-47,共4页Nonferrous Metals（Extractive Metallurgy)

基　　金：国家自然科学基金项目(51004008;21071014)

摘　　要：在熔盐中用钠热还原法直接还原NbCl5制备铌粉。采用XRD、FESEM和EDS对产品粉末的结构、形貌和成分进行检测。结果表明,在摩尔百分比组成为LiCl-10.0%NaCl-36.0%KCl、LiCl-44.2%KCl-5.3%CaCl2和LiCl-11.6%KCl-36.1%CaCl2的熔盐中均可获得纯纳米铌粉,经熔盐原位750℃热处理可以降低产品氧含量。Niobium powder was prepared by sodiothermic reduction process from NbC15 in different molten salts. The phases, morphology and elements of the niobium powder were analyzed by XRD, FESEM and EDS, respectively. The results show that fine and uniform niobium nanometer powder was successfully obtained in the molten salt systems of LiCI-10.0%NaC1-36.0%KCl（mole percent）, LiC1-44.2%KC1-5.3% CaC12 and LiCl-11.6%KC1-36.1%CaCl2, and the oxygen content of the obtained niobium powder decreases after in situ heat treatment in molten salts at 750℃.

关 键 词：钠热还原 金属铌粉 NbCl5 熔盐 