聚酚醚模塑料的研制  

Development and Preparation of Poly Phenol Ether Molding Plastics

作　　者：唐勇 李谦 张志平 胡卫东 

机构地区：[1]中蓝晨光化工研究设计院有限公司,四川成都610041

出　　处：《塑料工业》2012年第7期111-113,共3页China Plastics Industry

摘　　要：以聚酚醚树脂为基体树脂、六次甲基四胺为交联剂,再添加高温黏结剂、石英粉、玻纤等填料,在一定的工艺条件下共混,制得聚酚醚模塑料。研究了不同含量的交联剂、高温黏结剂等成分对聚酚醚模塑料力学性能和耐高温性能的影响。结果表明,六次甲基四胺的用量控制在聚酚醚树脂质量的4%～12%之间,填料的质量分数为60%～75%,其中高温黏结剂的质量分数为15%～20%,所制备的聚酚醚模塑料的各项性能较佳。With poly phenol ether resin as matrix resin,hexamethylenetetramine as cross-linking agent,by adding high temperature binder,quartz powder,glass fiber as filler,blending under certain conditions,poly phenol ether plastics were prepared.The effects of different content of cross-linking agents,high temperature binder on the mechanical properties and high temperature resistance of poly phenol ether molding plastic were studied.Results showed that the properties of the prepared poly phenol ether resin were the best when the amount of hexamethylenetetramine was 4%～12% as that of poly phenol ether,the mass fraction of the filler was 60%～75%,and the mass fraction of high temperature binder was 15%～20%.

关 键 词：聚酚醚 模塑料 

分 类 号：TQ323.1[化学工程—合成树脂塑料工业]