乳化沥青改性用丁苯胶乳凝胶质量分数影响因素研究  

The influence factors of styrene-butadiene latex gel content for emulsified asphalt modification

作　　者：李冬红[1] 肖瑞[1] 范永将[1] 李彤霞[1] 潘广勤[1] 

机构地区：[1]中国石油兰州石化公司研究院,甘肃兰州730060

出　　处：《化工科技》2012年第3期18-20,共3页Science & Technology in Chemical Industry

基　　金：中国石油天然气集团公司资助项目(2008B-3404-01)

摘　　要：采用复合乳化剂条件下,在过氧化物与亚铁盐组成的氧化还原体系引发作用下合成乳化沥青改性用丁苯胶乳,研究引发剂、乳化剂、相对分子质量调节剂及控温模式对胶乳中w(凝胶)的影响。结果表明,采用质量分数约4%乳化剂,0.1%～0.2%引发剂,0.225%～0.275%相对分子质量调节剂,并采用三段控温模式(初期温度16～20℃,中期温度28～30℃,后期温度38～40℃),可有效控制胶乳中的w(凝胶)。The styrene-butadiene latex for emulsified asphalt was synthesized by a complex emulsifier, with peroxide and ferrous salt as initiation system. The effects of initiator, emulsifier, molecular weight regulator and temperature control on gel content were discussed. The results showed the gel content could be effective controlled,using 4% emulsifier,0. 1%-0. 2% initiator,0. 225%-0. 275% molecular weight regulator and 3 stages temperature control （initial- 16 - 20 ℃, middle. 28 - 30 ℃, late.. 38-40℃）.

关 键 词：丁苯胶乳 乳化沥青 改性 凝胶 

分 类 号：TQ331.4[化学工程—橡胶工业]