硅酸铝钠复配体系涂布阻燃纸性能的研究  

Study on Fire Retardant Property of the Paper Coated the Combination System of Sodium Aluminum Silicate

作　　者：胡芳[1] 聂双喜[1] 欧阳昌礼[1] 荣毅[1] 叶昆朋[1] 宋海农[1] 

机构地区：[1]广西大学轻工与食品工程学院,广西南宁530004

出　　处：《中国造纸》2012年第7期22-25,共4页China Pulp & Paper

摘　　要：实验通过制定阻燃剂复配方案,研究了以硅酸铝钠(NaAl(SiO3)2)为主、用Mg(OH)2、Al(OH)3、膨润土、红磷部分取代NaAl(SiO3)2,验证了NaAl(SiO3)2为主的阻燃剂复配体系对涂布阻燃纸阻燃效果的影响。结果表明,这几种阻燃剂的协同阻燃效果明显,相对于单一NaAl(SiO3)2阻燃剂和其他复配阻燃剂,Mg(OH)2与NaAl(SiO3)2复配效果最好,当Mg(OH)2与NaAl(SiO3)2的质量比为1∶2、涂布量为63.2 g/m2时,涂布阻燃纸的炭化长度达到88 mm。In this paper, the quality of fire-retardant paper prepared by coating sodium aluminum silicate flame retardant system was evaluated. Sodium aluminum silicate with perfectly crystallized structure and thermal stahihty applies to paper can play a role in whitening and flame retardant. The results showed that the application of magnesium hydroxide, aluminum hydroxide, bentonite and red phosphorus combining with sodium aluminum silicate has a good synergistic flame retardant effect.