SYNTHESIS AND MAGNETIC PROPERTIES OF COMPLEXES OF A CONJUGATED HYPERBRANCHED POLYMER CONTAINING BITHIAZOLE RINGS  

作　　者：Neng-wen Ding 孙维林 Yan Lin Zhi-quan Shen 

机构地区：[1]Key Laboratory of Macromolecular Synthesis and Functionalization,Department of Polymer Science and Engineering,Zhejiang University,Hangzhou,310027,China [2]Ningbo City College of Vocational Technology,Ninbo,315100,China

出　　处：《Chinese Journal of Polymer Science》2012年第5期759-769,共11页高分子科学（英文版）

基　　金：financially supported by the National Natural Science Foundation of China(Nos.21174129 and 20674071)

摘　　要：A novel conjugated hyperbranched polymer containing bithiazole rings （PBTADB） was synthesized by polycondensation of 1,3,5-benzenetricarboxaldehyde and 2,2＇-diamino-4,4＇-bithiazole （DABT）. The structure of the hyperbranched polymer was confirmed by FT-IR and 1H-NMR. PBTADB dissolved in organic polar solvents such as DMSO and NMP. Bithiazole tings were introduced to provide bidentate N-donor sites for binding metal ions. The metal complexes were prepared by chelation of the polymer with Co2＋ and Sm3＋. The magnetic behavior of coolcdination compounds was measured as a function of magnetic field strength （0-4.8 ×106 A/m） at 5 K and as a fimetion of temperature （5-300 K） at magnetic field strength of 2.4×106 A/re. The magnetic hysteresis loops of PBTADB-Sm3＋ and PBTADB-Co2＋ showed the typical ＇S＇ shape at 5 K with the Curie-Weiss temperature To = 96 K and 41 K respectively. The results show that they exhibit properties of soft ferromagnetic materials.A novel conjugated hyperbranched polymer containing bithiazole rings （PBTADB） was synthesized by polycondensation of 1,3,5-benzenetricarboxaldehyde and 2,2＇-diamino-4,4＇-bithiazole （DABT）. The structure of the hyperbranched polymer was confirmed by FT-IR and 1H-NMR. PBTADB dissolved in organic polar solvents such as DMSO and NMP. Bithiazole tings were introduced to provide bidentate N-donor sites for binding metal ions. The metal complexes were prepared by chelation of the polymer with Co2＋ and Sm3＋. The magnetic behavior of coolcdination compounds was measured as a function of magnetic field strength （0-4.8 ×106 A/m） at 5 K and as a fimetion of temperature （5-300 K） at magnetic field strength of 2.4×106 A/re. The magnetic hysteresis loops of PBTADB-Sm3＋ and PBTADB-Co2＋ showed the typical ＇S＇ shape at 5 K with the Curie-Weiss temperature To = 96 K and 41 K respectively. The results show that they exhibit properties of soft ferromagnetic materials.

关 键 词：BITHIAZOLE Conjugated hyperbranched polymer Magnetic properties. 

分 类 号：O633.5[理学—高分子化学]