纤维状Ni粉前驱体草酸氨镍制备工艺研究  

Research on precursor synthesis processes fibrous nickel powder

作　　者：赵明[1] 赵国欣[1] 李领川[1] 王芳[1] 杨长春[2] 

机构地区：[1]中州大学实验管理中心,郑州450044 [2]郑州大学化学与分子工程学院,郑州450001

出　　处：《粉末冶金技术》2012年第3期206-213,共8页Powder Metallurgy Technology

摘　　要：纤维状Ni粉可通过纤维状草酸氨镍晶体热解制得。比较研究了直接沉淀法和沉淀转移法两种制备草酸氨镍的工艺。XRD、SEM、IR和TG的结果表明,两种方法制备草酸氨镍的晶体结构一致、晶体形貌均呈纤维状、均含有氨和草酸根。沉淀转移法制备草酸氨镍条件:c(Ni2+)为0.4～0.6 mol.L-1,温度70～80℃,pH值8.0～8.9,c(Ni2+)∶c(NH4+)=(1∶4)～(1∶3),反应时间30～40min,添加0.2%～0.5%(质量分数)PVP。能够在较宽范围内制备出纤维状草酸氨镍,同时能够对不合格产品进行回转,适合于工业化生产。Fibrous nickel powder can be made through thermolysis of the fibrous complex nickel oxalate crystal.Two preparation processes of complex nickel oxalate： direct precipitation process and precipitation transfer process were compared.The results from XRD,SEM,IR and TG show that the crystal structure of complex nickel oxalate by the two processes is consistent,crystal is fibrous and contains ammonia and oxalic acid root.The preparation conditions of the complex nickel oxalate for precipitation transfer process： c（Ni2＋） of 0.4-0.6 mol·L-1,temperature of 70-80 ℃,pH of 8.0-8.9,c（Ni2＋）∶ c（NH4＋） =（1∶ 4）-（1∶ 3）,the reaction time 30-40 min,additive of PVP0.2%-0.5%.

关 键 词：纤维状 草酸镍盐 配合物 工艺 

分 类 号：TQ175.79[化学工程—硅酸盐工业]