NPS-1负载磷钨酸催化合成4-叔丁基-2-(α-甲基苄基)苯酚  

Synthesis of 4-tert-butyl-2-(α-methyl benzyl)phenol catalyzed by NPS-1 supported phosphotungstic acid

作　　者：张晓利[1] 李显锋[1] 刘志玲 亢宇[3] 赵思源[3] 谢伦嘉[3] 

机构地区：[1]西北化工研究院,陕西西安710600 [2]陕西延长石油(集团)有限责任公司研究院,陕西西安710075 [3]中国石化北京化工研究院,北京100013

出　　处：《工业催化》2012年第8期68-71,共4页Industrial Catalysis

摘　　要：以介孔分子筛NPS-1负载12-磷钨酸杂多酸为催化剂,4-叔丁基苯酚和苯乙烯为原料,合成4-叔丁基-2-(α-甲基苄基)苯酚(t-BAMBP)。采用正交实验研究介孔材料NPS-1负载12-磷钨酸对t-BAMBP合成反应的催化活性,考察反应温度、反应时间、原料配比和催化剂用量对t-BAMBP收率的影响。优化的工艺条件为:反应温度70℃,反应时间30 min,n(苯乙烯)∶n(4-叔丁基苯酚)=1.3∶1,催化剂用量为4-叔丁基苯酚质量的0.2%,t-BAMBP收率70.3%。4-Tert-butyl-2- （α -methyl benzyl ） phenol （ t-BAMBP ） was synthesized based on 4-tert-butyl- phenol and styrene as the raw materials in the presence of NPS-1 supported phosphotungstic acid （H3PO4 · 12WO3/NPS-1 ）. The catalytic activity of H3PO4 · 12WO3/NPS-1 was investigated by orthogonal test. The effect of reaction temperature, reaction time, ratio of the reactants and catalyst dosage on the yield of t-BAMBP was studied. The results showed that the yield of t-BAMBP reached 70.3% under the optimum condition as follows ： reaction temperature 70 ~C, reaction time 30 min, n （styrene） ： n （4-tert-butyl- phenol） = 1.3： 1, and catalyst dosage 0.2% of 4-tert-butylphenol mass.

关 键 词：催化化学 4-叔丁基-2-(α-甲基苄基)苯酚 介孔分子筛 H3PO4.12WO3/NPS-1催化剂 12-磷钨酸 

分 类 号：TQ426.94[化学工程] O643.36[理学—物理化学]