高岭土微球原位晶化合成L沸石与表征  

In-situ synthesis and characterization of zeolite L from kaolin-microspheres

在线阅读下载全文

作  者:汪毅 樊红超 张忠东 陈宜俍[2] 

机构地区:[1]中国石油兰州化工研究中心,甘肃兰州730000 [2]郑州大学化工与能源学院,河南郑州450001

出  处:《工业催化》2012年第9期36-39,共4页Industrial Catalysis

摘  要:采用水热晶化法在高岭土微球上原位合成L沸石,考察相对结晶度和堆积密度的关系,通过XRD、IR、BET和SEM对合成产品的晶态结构进行表征和形貌观察。结果表明,合成样品的比表面积为171.38 m2.g-1,平均孔径为2.855 nm。相对结晶度为34%~54%时,堆积密度随着相对结晶度的升高由0.80 g.cm-3降至0.64 g.cm-3,合成L沸石晶粒为柱状,生长在高岭土微球表面。Zeolite L was synthesized in-situ on kaolin microspheres by hydrothermal crystallization method. The relationship of relative crystallinity and bulk density was investigated. The as-prepared zeolite samples were characterized by XRD, IR, BET and SEM. The results showed that the surface area and average pore diameter of zeolite L wets 171.38 m2 · g^- 1 and 2. 855 nm, respectively, and the bulk density of zeolite L decreased from 0.80 g · cm -3 to 0.64 g · cm-3 with the increase of the relative crystallinity from 34% to 54%. The crystal phase of the as-prepared zeolite samples was column, and their grains grew on the surface of kaolin-microspheres.

关 键 词:催化剂工程 高岭土微球 原位晶化 相对结晶度 堆积密度 

分 类 号:TQ426.6[化学工程] TQ424.25

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象