淬火温度对AMS 6308钢组织和性能的影响  

Effect of Quenching Temperature on Structure and Mechanical Properties of AMS 6308 Steel

作　　者：刘宝锋[1,2] 杨钢[2] 华建社[1] 杨沐鑫[2] 

机构地区：[1]西安建筑科技大学冶金工程学院,西安710055 [2]钢铁研究总院结构材料研究所,北京100081

出　　处：《特钢技术》2012年第3期12-17,共6页Special Steel Technology

摘　　要：研究了淬火处理(900℃～1010℃)对AMS6308钢(wt.%:0.1C、1.0Cr、1.97Ni、3.25Mo、2.0Cu、0.08V、0.83Si、Fe余量。)微观组织和力学性能的影响,结果表明,试验钢在915℃×0.5h油冷+(-80℃)×1h+205℃×2h回火后得到最佳的力学性能(Rm=1135MP,Rp0.2=880MP,A=16%,Z=63%,AKV2>125J,HRC=35)。The effects of Quenching treatment at900℃-1010℃,cool treating at -80 ℃ and tempering at 205 ℃ on microstructure of steel AMS 6308 （wt.% 0.1 C, Cr 1.0, 1.97 Ni, 3.25 Mo, 2.0 Cu, 0.08 V, 0.83 Si, 0.001 P, 0.004 S, Fe, Balance ） and mechanical properties of steel has been studied. Results show that with oil quenched at 915 ℃ for 0.5 h ＋ cool treated at -80 ℃ for lh ＋ tempered at 205 ℃ for 2 h, steel AMS 6308 has excellent integrated mechanical properties（Rm - 1 135 MPa, Rp0.2 = 880 MPa, A = 16%, Z = 63%, AKv2 〉 125 J, HRC = 35）.

关 键 词：AMS6308钢 淬火温度 M6C沉淀相 力学性能 

分 类 号：TG156.3[金属学及工艺—热处理]