Influence of annealing treatment on as-grown Ib-type diamond crystal at a high temperature and high pressure  

作　　者：黄国锋 尹辑文 白洪波 胡义嘎 凯丽 静婧 马红安 贾晓鹏 

机构地区：[1]Department of Physics and Electronic Engineering,Chifeng College [2]National Laboratory of Superhard Materials,Jilin University

出　　处：《Chinese Physics B》2012年第10期491-495,共5页中国物理B（英文版）

基　　金：Project supported by the National Natural Science Foundation of China (Grant Nos. 50572032 and 50731006)

摘　　要：In this paper,we report on the influence of annealing treatment on as-grown Ib-type diamond crystal under high pressure and high temperature in a china-type cubic anvil high-pressure apparatus.Experiments are carried out at a pressure of 7.0 GPa and temperatures ranging from 1700 C to 1900 C for 1 h.Annealing treatment of the diamond crystal shows that the aggregation rate constant of nitrogen atoms in the as-grown Ib-type diamond crystal strongly depends on diamond morphology and annealing temperature.The aggregation rate constant of nitrogen remarkably increases with the increase of annealing temperature and its value in octahedral diamond is much higher than that in cubic diamond annealed at the same temperature.The colour of octahedral diamond crystal is obviously reduced from yellow to nearly colorless after annealing treatment for 1 h at 1900 C,which is induced by nitrogen aggregation in a diamond lattice.The extent of nitrogen aggregation in an annealed diamond could approach approximately 98% indicated from the infrared absorption spectra.The micro-Raman spectrum reveals that the annealing treatment can improve the crystalline quality of Ib-type diamond characterized by a half width at full maximum at first order Raman peak,and therefore the annealed diamond crystals exhibit nearly the same properties as the natural IaA-type diamond stones of high quality in the Raman measurements.In this paper,we report on the influence of annealing treatment on as-grown Ib-type diamond crystal under high pressure and high temperature in a china-type cubic anvil high-pressure apparatus.Experiments are carried out at a pressure of 7.0 GPa and temperatures ranging from 1700 C to 1900 C for 1 h.Annealing treatment of the diamond crystal shows that the aggregation rate constant of nitrogen atoms in the as-grown Ib-type diamond crystal strongly depends on diamond morphology and annealing temperature.The aggregation rate constant of nitrogen remarkably increases with the increase of annealing temperature and its value in octahedral diamond is much higher than that in cubic diamond annealed at the same temperature.The colour of octahedral diamond crystal is obviously reduced from yellow to nearly colorless after annealing treatment for 1 h at 1900 C,which is induced by nitrogen aggregation in a diamond lattice.The extent of nitrogen aggregation in an annealed diamond could approach approximately 98% indicated from the infrared absorption spectra.The micro-Raman spectrum reveals that the annealing treatment can improve the crystalline quality of Ib-type diamond characterized by a half width at full maximum at first order Raman peak,and therefore the annealed diamond crystals exhibit nearly the same properties as the natural IaA-type diamond stones of high quality in the Raman measurements.

关 键 词：high pressure and high temperature diamond crystal ANNEALING nitrogen aggregation 

分 类 号：TQ164[化学工程—高温制品工业]