刚玉细粉对镁质浇注料性能的影响  

Effect of corundum powder on properties of magnesian castable

作　　者：贾江议[1] 白剑伟 

机构地区：[1]河南科技大学材料科学与工程学院,洛阳471003 [2]郑州华宇耐材有限公司,郑州451251

出　　处：《耐火与石灰》2012年第5期1-3,10,共4页Refractories & Lime

摘　　要：以电熔镁砂为主要原料,通过改变刚玉细粉的加入量,在110℃、24h烘干及1 500℃、3h烧成制度下,研究了刚玉细粉的加入量对镁质浇注料性能的影响。结果表明,当刚玉细粉的加入量大于或小于6%时,镁质浇注料显气孔率大、耐压强度低、抗渣性能差。当刚玉细粉加入量为6%时,镁质浇注料综合性能优良。By taking electro-fused magnesia as raw material, the effects of adding amounts of corundum powder on the properties of magnesian castable are studied through the changes of adding amount of corundum and with the heating schedule of drying at 110℃ for 24h and firing at 1 500℃ for 3h, The re- suits show that when the adding amounts of corundum are higher or less than 6%, the magnesian castable has higher apparent porosity, lower crushing strength and poor slag resistance. When the adding amount of corundum powder is 6%, the comprehensive properties of the magnesian castable are good in oualitv.

关 键 词：镁质浇注料 刚玉细粉 电熔镁砂 性能 

分 类 号：TQ175.713[化学工程—硅酸盐工业]