Manufacture of Organic Glass Crafts by Polymerization Process at Normal Temperature

作　　者：尹沾合[1] 

机构地区：[1]广西工业职业技术学院石油与化学工程系,广西南宁530001

出　　处：《现代塑料加工应用》2012年第5期14-16,共3页Modern Plastics Processing and Applications

摘　　要：采用紫外光间歇照射引发甲基丙烯酸甲酯(MMA)反应,频率为照射3 min歇息30 min,光引发剂加入量为单体质量的0.12%,每次加料厚度1～3cm,常温过程(≤40℃)制作有机玻璃工艺品。结果发现,该法单体损失率仅为热引发法的14.8%,且适用于40℃以上易变形的内嵌物,电能消耗也大幅下降。Methyl methacrylate（MMA） was initiated by UV intermittent radiation. Each of radiation time was 3 min, the rest time was 30 min. The mass ratio of photo initiator（based on monomer） was 0.12%. The thickness of feeding is 1-3 cm. Then the organic glass crafts could be made at normal temperature （≤40 C）. The results show that its monomer loss rate is 14.8% of thermal initiation. And it is suitable to embed deforming material（~40 C）. Power consumption decreases sharply.