不同聚合工艺低融嵌段共聚聚丙烯产品结构性能研究  

Structure and Properties Investigation of Different Processes Low-melting-block Co-polypropylene

作　　者：田广华 宋彩霞 

机构地区：[1]神华宁夏煤业集团煤炭化学工业公司研发中心,宁夏银川750411

出　　处：《塑料工业》2012年第10期77-79,共3页China Plastics Industry

摘　　要：采用力学测试、偏光分析和扫描电镜分析等手段,分别对Spheripol、Novolen和Innovene三种不同工艺的低融嵌段共聚聚丙烯产品EPS30R、2500H和K8303进行了结构性能分析。结果表明:Novolen和Innovene气相法工艺,在聚合反应过程中,对产品的球晶尺寸和橡胶相分布具有很好的控制效果,能够通过降低球晶尺寸提高橡胶相的分散均匀性,有效提高产品的冲击性能。By the means of mechanical testing, analysis of polarizing microscope and SEM, the structure and properties of EPS30R （ Spheripol）, 2500H （Novolen） and K8303 （Innovene） of low-melting-block co-polypropylene with different polymerization processes were researched. The results showed that, in the polymerization process, Novolen and Innovene gas-phase process can control the crystallite size and rubber distribution of the product better, improve the product impact performance effectively by miniaturizing the crystallite and increasing the dispersed rubber phase.

关 键 词：聚丙烯 聚合工艺 球晶尺寸 橡胶相 