Microwave Absorption and Shielding Property of Composites with FeSiAl and Carbonous Materials as Filler  

作　　者：Wenqiang Zhang Yonggang Xu Liming Yuan Jun Cai Deyuan Zhang 

机构地区：[1]Bionic and Micro/Nano/Bio Manufacturing Technology Research Center,School of Mechanical Engineering and Au-tomation,Beihang University,Beijing 100191~China

出　　处：《Journal of Materials Science & Technology》2012年第10期913-919,共7页材料科学技术（英文版）

基　　金：supported by the National Natural Science Foundation of China (No. 50805005);the National High Technology Research and Development Program of China ("863 Program", No. 2009AA043804);the Foundation for the Author of National Excellent Doctoral Dissertation of PR China (No. 2007B32);the Innovation Foundation of BUAA for Ph.D. Graduates

摘　　要：Silicone rubber composites filled with FeSiAI alloys and multi-walled carbon nanotubes （MWCNT）/graphite have been prepared for the first time by a coating process. The complex permittivity and permeability of the composites were measured with a vector network analyzer in a 1-4 GHz frequency range, and the DC electric conductivity was measured by a standard four-point contact method. These parameters were then used to calculate the reflection loss （RL） and shielding effectiveness （SE） of the composites. The results showed that the added MWCNT increased the permittivity and permeability of composites in the L-band, while the added graphite increased only the permittivity. The variation lies in the interactions between two carbonous absorbents. Addition of 1 wt% MWCNT enhanced the RL in the L-band （minimum -5.7 dB at 1 ram, -7.3 dB at 1.5 ram）, while the addition of graphite did not. Addition of MWCNT as well as graphite reinforced the shielding property of the composites （maximum SE 13.3 dB at 1 ram, 18.3 dB at 1.5 ram） owing to the increase of conductivity. The addition of these carbonous materials could hold the promise of enforcing the absorption and shielding property of the absorbers.Silicone rubber composites filled with FeSiAI alloys and multi-walled carbon nanotubes （MWCNT）/graphite have been prepared for the first time by a coating process. The complex permittivity and permeability of the composites were measured with a vector network analyzer in a 1-4 GHz frequency range, and the DC electric conductivity was measured by a standard four-point contact method. These parameters were then used to calculate the reflection loss （RL） and shielding effectiveness （SE） of the composites. The results showed that the added MWCNT increased the permittivity and permeability of composites in the L-band, while the added graphite increased only the permittivity. The variation lies in the interactions between two carbonous absorbents. Addition of 1 wt% MWCNT enhanced the RL in the L-band （minimum -5.7 dB at 1 ram, -7.3 dB at 1.5 ram）, while the addition of graphite did not. Addition of MWCNT as well as graphite reinforced the shielding property of the composites （maximum SE 13.3 dB at 1 ram, 18.3 dB at 1.5 ram） owing to the increase of conductivity. The addition of these carbonous materials could hold the promise of enforcing the absorption and shielding property of the absorbers.

关 键 词：Absorbing materials ELECTROMAGNETIC Reflection loss Shielding effectiveness 

分 类 号：TN915.06[电子电信—通信与信息系统] TQ165[电子电信—信息与通信工程]