乙烯基改性聚硅氧烷乳液的制备  

Preparation of vinyl modified polysiloxane emulsion

作　　者：王小娟[1] 

机构地区：[1]陕西工业职业技术学院,陕西咸阳712000

出　　处：《印染助剂》2012年第11期27-29,共3页Textile Auxiliaries

摘　　要：以八甲基环四硅氧烷(D4)与乙烯基三乙氧基硅氧烷(A-151)为单体,十二烷基硫酸钠(SDS)和脂肪醇聚氧乙烯醚(AEO9)为复合乳化剂,十二烷基苯磺酸作催化剂,制备了性能稳定的乙烯基改性聚硅氧烷乳液.讨论了乳化剂、催化剂、硅烷偶联剂用量,反应温度,反应时间等因素对聚合反应的影响.结果表明:当乳化剂用量4%(对单体总质量),催化剂用量8%(对D4质量),硅烷偶联剂用量5%(对D4质量),反应温度75℃,反应时间3 h时,所得聚合物乳液的稳定性较好,单体转化率也比较高.A stable vinyl modified polysiloxane emulsion was prepared with octamethyl cyclotetrasiloxane （D4） and vinyl triethoxysiloxane （A-151） as monomers, sodium dodecylsulfate （SDS） and polyoxyethylene alkyl ether （AEO9） as complex emulsifiers, dodecylbenzene sulfonic acid as catalyst. The effects of emulsifier, cata- lyst, coupling agent, reaction temperature and time on polymerization reaction were discussed. The results showed that when the amount of emulsifier was 4% （on the mass of monomer）, the amount of catalyst was 8%（on the mass of D4）, the amount of coupling agent was 5%（on the mass of D4）, reaction temperature was 75℃, reaction time was 3 h, the obtained emulsion had good stability and high monomer conversion.

关 键 词：八甲基环四硅氧烷 乙烯基三乙氧基硅氧烷 乙烯基聚硅氧烷乳液 

分 类 号：TQ264.17[化学工程—有机化工]