浸溶胶对RH炉用镁铬砖气孔特性的影响研究  

Studies on Effect of Impregnation with Sols on Pore Characteristic of Magnesia Chromite Brick Used in RH

作　　者：陈希来[1,2] 邹龙[1] 曹锟 宋仪杰 李亚伟[2] 徐国涛[1] 

机构地区：[1]武汉钢铁(集团)公司研究院,武汉430080 [2]武汉科技大学耐火材料与高温陶瓷湖北省重点实验室,武汉430081 [3]武钢炼钢总厂二分厂,武汉430080 [4]武钢耐火材料有限公司,武汉430080

出　　处：《材料导报》2012年第22期122-124,共3页Materials Reports

基　　金：博士后项目资助

摘　　要：研究了浸铝溶胶、锆溶胶镁铬砖的气孔特性变化及对抗渣性能的影响。结果表明:浸溶胶后镁铬砖的气孔率减小、气孔孔径分布变好,确定合适的溶胶浸渍次数为3～4次;浸溶胶会提高镁铬砖的抗渣性能,铝溶胶更能提高材料的抗渣渗透性而锆溶胶则更能改善材料的抗渣侵蚀性。Pore characteristic evolution and slag resistance of magnesia chromite brick impregnated with amumi na sol and zirconia sol were studied. The results indicate that the porosity decreases and pore size distribution becomes better after the specimens impregnated with sols. The appropriate impregnation times is 3 or 4. The slag resistance characteristic is improved after the specimens impregnated with sols. Alumina sol can be beneficial to enhance the slag anti-penetration and zirconia sol is better to improve the slag anti-corrosion.

关 键 词：镁铬砖 气孔特性 抗渣性 氧化铝溶胶 氧化锆溶胶 

分 类 号：TF065.1[冶金工程—冶金物理化学]