早强剂在膏体充填中的作用机理及其应用研究  

Research on mechanism and application of early strength agent in paste backfill

作　　者：肖云涛[1] 王洪江[2] 周晓东[1] 焦华喆[2] 刘晓辉[2] 吴爱祥[2] 

机构地区：[1]武汉钢铁集团矿业有限责任公司 [2]北京科技大学土木与环境工程学院

出　　处：《黄金》2012年第11期29-33,共5页Gold

基　　金：国家自然科学基金资助项目(50934002;51104011);长江学者和创新团队发展计划项目(IRT 0950);中国博士后科学基金资助项目(201104053;20100480200)

摘　　要：缩短充填料浆的凝结时间是提高充填体早期强度、降低充填成本的有效途径之一。为此,开展了早强剂在膏体充填中的应用研究。试验表明,充填料浆中添加水玻璃能满足采场对膏体凝结的要求。工业试验表明,添加10%水玻璃后膏体最终初凝时间为450 min,采场终凝时间为3 d。To increase the early strength of the paste filling and decrease filling cost,shortening the setting time of the backfill paste is one of the effective ways.To confirm it,early strength agent in paste filling was applied and studied.The results showed that the addition of sodium silicate to the paste can meet the standard of paste setting in stopes.Moreover,the industrial test showed that with the addition of 10 % sodium silicate,the initial setting time of the paste was 450 min,while the final setting time was 3 days.

关 键 词：膏体充填 早期强度 早强剂 水玻璃 

分 类 号：TD853.343[矿业工程—金属矿开采]