稀土发光涂料耐磨性配方研究  

The Research of Wear-resisting Formula of Rare Earth Luminescent Coating

作　　者：高珊珊[1] 王明媚[1] 唐安江[1] 

机构地区：[1]贵州大学化学与化工学院,贵州贵阳550025

出　　处：《广州化工》2012年第22期81-83,共3页GuangZhou Chemical Industry

摘　　要：采用正交试验方法设计配方方法,使用市售的稀土发光材料SrAl2O4:Eu2+,环氧树脂、PU、三氧化二铝作为正交因子,各有三个水平。以环氧聚胺酯涂料的耐磨性作为研究对象,采用正交表L9(34)组织试验,得到耐磨性最佳的发光涂料的配方。Using orthogonal test,the method of coating formula was designed.Commercially available rare earth luminescent material SrAl2O4：Eu2＋,epoxy resin,PU,and aluminum oxide were orthogonal factors,and each factor had three levels.For improving wear-resistance of epoxy polyurethane coating,the experiments were arranged according to the orthogonal table of L9（34）,l and the best formula of wear-resistance formula of the luminescent coating was found.

关 键 词：耐磨性 发光材料 涂料 正交试验 

分 类 号：TQ630.7[化学工程—精细化工]