超高分子量聚乙烯纤维预辐照接枝丙烯酸甲酯  

Preirradiation graft copolymerization of methyl acrylate onto ultra-high molecular weight polyethylene fiber induced byγ-rays

作　　者：魏寒[1] 邢哲[2] 王谋华[2] 吴国忠[2] 沈青[1] 

机构地区：[1]东华大学材料科学与工程学院,上海201620 [2]中国科学院上海应用物理研究所,上海201800

出　　处：《辐射研究与辐射工艺学报》2012年第6期328-332,共5页Journal of Radiation Research and Radiation Processing

基　　金：国家自然科学基金(10905088)资助

摘　　要：采用预辐照接枝的方法研究了丙烯酸甲酯(MA)单体在超高分子量聚乙烯(UHMWPE)纤维表面的接枝聚合反应。考察了吸收剂量、单体浓度、接枝聚合反应温度对接枝率的影响。结果表明:UHMWPE纤维接枝MA的接枝率较高,最高可达约151%,接枝率随吸收剂量、单体浓度、反应温度升高而增加。用红外光谱法分析了接枝前后纤维官能团的变化,通过扫描电镜观察了接枝前后纤维表面的形貌。Methyl acrylate （MA） monomer was grafted onto ultra-high molecular weight polyethylene （UHMWPE） fibers after irradiation by y-rays. The effects of absorption dose, monomer concentration and temperature on the degree of grafting （DG） were investigated. The grafting yield of MA reached to a considerable degree, approximately 151% at the maximum value. The DG of MA on UHMWPE fibers increased with the increment of absorption dose, temperature and concentration of MA. The function groups and morphologies of the

关 键 词：超高分子量聚乙烯 丙烯酸甲酯 辐射接枝 

分 类 号：TQ342[化学工程—化纤工业] O611[理学—无机化学]