不同注塑方法及HDPE/iPP共混物组成对附生结晶的影响  

The Influence of Product Scale Effect and Its Composition on the Formation of Epitaxial Structure of HDPE/iPP Blends

作　　者：邓鹏[1] 张蕾[1] 刘洪[1] 张杰[1] 

机构地区：[1]四川大学高分子科学与工程学院高分子材料工程国家重点实验室,四川成都610065

出　　处：《塑料》2012年第6期50-53,45,共5页Plastics

摘　　要：主要研究了等规聚丙烯/高密度聚乙烯共混物中等规聚丙烯含量和不同注塑成型方法对附生结晶的影响。实验中分别利用微注塑成型和普通注塑成型获得不同尺度的样品,并且利用差示扫描量热法(DSC)和二维广角X射线衍射(2D-WAXD)对制品的结晶行为进行了研究。实验结果表明:微注塑成型方法与具有相对较高聚丙烯含量的结合有利于高密度聚乙烯/等规聚丙烯共混物中附生结晶的产生。The present study focused on the importance of different injection molding and iPP content to the formation of epitaxial structure formed in injection-molded bars of high-density polyethylene （HDPE）/isotactic polypropylene （iPP） blends. The injection-molded bars were prepared via micro and conventional injection molding, respectively. Differential scanning calorimetry （DSC） and wide-angle X-ray diffraction （WAXD） were used to investigate their morphological and crystal features. The results indicated that an appropriate matching of micro-part and relative high iPP content was more favorable for epitaxial crystallization.

关 键 词：等规聚丙烯 高密度聚乙烯共混物 注塑成型 等规聚丙烯含量 附生结晶 取向度 

分 类 号：TB332[一般工业技术—材料科学与工程]