双核离子液体的合成及其对酯化反应的催化活性  

Synthesis of Binuclear Ionic Liquids and Their Catalytic Activity for Esterification

作　　者：赵地顺[1] 刘猛帅[1] 葛京京[1] 张娟[1] 任培兵[1,2] 

机构地区：[1]河北科技大学化学与制药工程学院,石家庄050018 [2]石家庄焦化集团有限责任公司,石家庄050031

出　　处：《有机化学》2012年第12期2382-2389,共8页Chinese Journal of Organic Chemistry

基　　金：国家自然科学基金(Nos.20576026,21106032);河北科技大学2012年度大学生科技创新基金资助项目~~

摘　　要：合成了双-(3-甲基-1-咪唑)亚丁基双对甲苯磺酸盐(Im-PTSA)、双-(3-甲基-1-咪唑)亚丁基双硫酸氢盐(Im-HSO4)、双-(1-吡啶)亚丁基双对甲苯磺酸盐(Py-PTSA)、双-(1-吡啶)亚丁基双硫酸氢盐(Py-HSO4)等4种功能化双核离子液体.分别采用红外光谱(FT-IR)、核磁共振氢谱(1H NMR)对合成的离子液体进行结构分析;采用热重(TG)测试了离子液体的热稳定性;此外,考察了离子液体的酸性和溶解性.以丁二酸和乙醇的酯化反应考察了4种离子液体的催化活性,结果表明:当n(C4H6O4)∶n(C2H5OH)=1∶3,催化剂Im-PTSA量占总质量的1.90%,反应温度70℃,反应时间2.5 h,酯收率可达93.6%,选择性达100%,且离子液体经真空干燥重复使用8次,催化活性没有明显降低.以奥氏体316 L不锈钢为试样,考察了双核功能化离子液体的腐蚀性,与浓硫酸进行对比,其对钢试样的腐蚀率不到浓硫酸的1/10.以双-(3-甲基-1-咪唑)亚丁基双对甲苯磺酸盐(Im-PTSA)为催化剂,考察了一元有机酸和二元有机酸与系列醇的酯化反应,均获得较高的酯收率和选择性,反应结束后产品与催化剂自动分层,简化了分离,有望成为一种具有发展潜力的酯化催化剂.A series of functional binuclear ionic liquids based on bis-（3-methyl-l-imidazole）butylidene double P-toluene sul- fonic acid salt （Im-PTSA）, bis-（3-methyl-l-imidazole）butylidene double bisulfate （Im-HSO4）, bis-（1-pyridine）butylidene dou- ble p-toluene sulfonic acid salt （Py-PTSA）, bis-（1-pyridine）butylidene double bisulfate （Py-HSO4） were synthesized by a two-step proceeding and their structures were characterized by FT-IR and IH NMR spectra. Their thermal stabilities were characterized by TG. In addition, the acidity and solubility of functional binuclear ionic liquids were also studied. The catalytic activity of the binuclear ionic liquids for the esterification of succinic acid with ethanol was measured. The results show that under the optimized conditions of n（succinic acid） ： n（ethanol）-- 1 ＂ 3, catalyst used dosage 1.90% （wt）, 70 ~C and 2.5 h, the yield of dietbyl succinate reached 93.6% and the selectivity was near up to 100%. Im-PTSA was reused at least 8 times with- out significant decrease in activity after drying under vacuum. Austenitic stainless steel 316L was used for conducting the cor- rosion test under the above esterificaion condition, the corrosion rates of the steel plates dipped in the systems with these ionic liquids were less than one tenth of that with sulfuric acid. Fischer esterification of monocarboxylic acids and dicarboxylic ac- ids with different alcohols was observed on using Im-PTSA as catalyst which gave high product yield and selectivity. Use of such a reaction catalyst should be appreciated for its convenient separation.

关 键 词：双核离子液体 酯化反应 催化剂 丁二酸二乙酯 腐蚀性 

分 类 号：O643.3[理学—物理化学]