环保型高强力再生胶微波辐射工艺的研究  

Study on microwave radiation process of environmental protection and high-strength reclaimed rubber

作　　者：王艳秋[1] 周立雪[1] 谢德伦 寇景[1] 姚亮[1] 

机构地区：[1]徐州工业职业技术学院材料工程学院,江苏徐州221140 [2]徐州华辰胶带有限公司,江苏徐州221000

出　　处：《应用化工》2012年第12期2085-2087,2090,共4页Applied Chemical Industry

基　　金：江苏省徐州市科技基金资助项目(XC10B002)

摘　　要：对再生原料进行预处理,选择合理的微波辐射方法再生。结果表明,微波再生的最佳工艺条件为微波辐射时间100 s,温度160℃和功率480 W,再生胶的拉伸强度和扯断伸长率能分别达到18.74 MPa和443.00%。胶片表面光洁,质地均匀,适合压延、压出工艺。The raw material used for microwave regeneration must be conducted by pretreatment select reasonably microwave radiation regeneration. The results showed that the microwave regeneration optimum process condition were as follows： microwave radiation time was 100 s, temperature was 160 ℃ and the power was 480 W. The tensile strength and elongation of the reclaimed rubber can respectively reach 18.74 MPa and 443.00%, the film surface smooth, uniform texture, suitable for rolling and extruding process.

关 键 词：微波辐射 环保高强力再生胶 工艺方法 工艺流程 工艺条件 