Failure analysis of the aluminum alloy tube in radiator of air conditioner

在线阅读下载全文

作  者:谭立新[1] 梁泰然[1] 陈强[1] 蔡一湘[1] 丁燕[1] 

机构地区:[1]广东省工业技术研究院(广州有色金属研究院),广东广州510650

出  处:《材料研究与应用》2012年第4期279-281,共3页Materials Research and Application

摘  要:通过对空调器室外散热器连接铝管的裂纹形貌、材料成分、金相组织、显微硬度等进行分析,表明失效铝管的组织均匀,没有明显的成分偏析,没有腐蚀性产物及腐蚀性元素;材料成分符合GB/T3190-2008《变形铝及铝合金化学成分》对铝合金牌号3003材料的要求;连接铝管因受到外界拉应力作用而产生裂纹,最终导致空调器冷媒渗漏.The crack reason of the aluminum tube connected with air conditioner was analyzed by morphologies observation of crack,chemical composition analysis,metallographic observation,Vickers hardness testing.The results show that the microstructure of aluminum tube is homogeneous.There is no obvious segregation,no corrosion products or corrosion elements in it.The material composition accords with the requirements of GB/T 3190-2008 'Wrought aluminium and aluminium alloy chemical composition'.The crack of aluminum alloy tube was caused by the tensile stresses from the outside,and finally it lead to the leakage of refrigerant in the air conditioner.

关 键 词:断裂分析 铝合金管 失效分析 

分 类 号:TG111.91[金属学及工艺—物理冶金]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象