聚2,5-呋喃二甲酸乙二醇酯的合成与表征  

SYNTHESIS AND CHARACTERATION OF POLY(ETHYLENE 2,5-FURANDICARBOXYLATE)

作　　者：姜敏[1] 刘茜[1] 李洋[1] 张强[1] 周光远[1] 

机构地区：[1]中国科学院长春应用化学研究所生态环境高分子材料重点实验室,长春130022

出　　处：《高分子学报》2013年第1期24-29,共6页Acta Polymerica Sinica

基　　金：国家自然科学基金青年科学基金(基金号51103152)资助项目

摘　　要：以2,5-呋喃二甲酸和乙二醇为原料,草酸亚锡为催化剂,通过直接酯化法合成了线性高分子量聚2,5-呋喃二甲酸乙二醇酯(PEF).运用红外光谱(FTIR)和核磁共振氢谱(1H-NMR)表征了该聚酯的结构;由乌氏黏度计法和凝胶渗透色谱(GPC)建立了该聚酯在一种混合溶剂体系中特性黏数和重均分子量的关系:[η]=2.82×10-6Mw0.99dL/g,25℃,苯酚-四氯乙烷(1∶1,W/W);示差扫描量热法(DSC)和热失重分析(TGA)测定了该聚酯的热转变性能,结果表明该聚酯玻璃化转变温度为84℃,熔点为211℃,起始热分解温度高于370℃,具有良好的热稳定性;运用旋转流变仪研究了PEF的流变性能,结果表明,PEF熔体属于假塑性流体,随相对分子量的减小和温度升高,其非牛顿指数增大,在高于PEF熔点20～40℃,剪切速率为2.17×10-2～1.14×102s-1时,PEF的非牛顿指数为0.85左右.Poly（ethylene 2,5-furandicarboxylate） （PEF） was synthesized via direct esterification method based on 2,5-furanicarboxylica acid and ethylene glycol.Stannous oxalate was used as catalyst.The results showed that the direct esterification method was a straightforward and convenient effective way for preparing PEF.The results of Fourier transform infrared spectroscopy （FTIR） and nuclear magnetic resonance spectroscopy （1H-NMR） confirmed the expected PEF structure.The results of Ubbelohde viscosity method and gel permeation chromatography （GPC） declared the relationship between intrinsic viscosities and weight-average molecular weight was [η]=2.82×10-6 Mw0.99 [dL/g,25℃,phenol-tetrachloroethane （1∶1,W/W）]; The results of differential scanning calorimeter （DSC） displayed that the glass transition （Tg） of PEF was 84℃ which was 16 K higher than that of poly（ethylene terephthalate） （PET） and the melting temperature （Tm） of PEF was 211℃ which was 43 K lower than that of PET.The results of thermogravimetric analysis （TGA） showed that the PEF was thermally stable up to 373℃.PEF had good thermal properties and was similar to that of PET.The results of coaxial cylinder viscometer showed that the PEF melt was a pseudoplastic Newtonian fluid and its Non-Newtonian index increased with decreasing of relative molecular weight and increasing of temperature.Non-Newtonian index was about 0.85 （melting temperature=230~250℃,rate of shear=2.17×10-2~1.14×102 s-1）.

关 键 词：2 5-呋喃二甲酸 聚2 5-呋喃二甲酸乙二醇酯 直接酯化法 合成与表征 

分 类 号：O633.5[理学—高分子化学]