1Cr11Co3W3NiMoVNbNB短时持久差异分析研究  

Analysis between the Results of the Short-term Rupture Test for 1Cr11Co3W3NiMoVNbNB

作　　者：江雷[1] 陈巳漪[1] 

机构地区：[1]东方汽轮机有限公司,四川德阳618000

出　　处：《东方汽轮机》2012年第4期33-40,共8页Dongfang Turbine

摘　　要：为深入分析1Cr11Co3W3NiMoVNbNB真空热处理后短时持久差异较大情况,对典型的同批次差异较大持久试样进行组织、断口、硬度试验分析,得出:1Cr11Co3W3NiMoVNbNB短时持久断口为典型的延性断口;短时持久不合格的主要原因是在高温持久试验温度下发生了材料的高温硬度较快的下降,并从下降幅度最大的位置产生裂纹并扩展直至断裂。In order to analysis deeply the different results of the short-term rupture samples for 1Cr11Co3W3NiMoVNbNB after vacuum heat treatment, tests for the organization, fracture and hardness of the sample are analysed in same batch.The test results show that short-term rupture fracture morphology of 1Cr11Co3W3NiMoVNbNB is ductile fracture, and the reason for short-term rupture failure mainly due to the high-temperature hardness of the material decline quickly, cracks usually grow in the location, which the hardness drop in maximum, and extend until fracture.

关 键 词：短时持久 1Cr11Co3W3NiMoVNbNB 碳化物粗化 

分 类 号：TG156.95[金属学及工艺—热处理]