水热法掺铌KTiOPO_4晶体的形貌和缺陷研究  

Morphology and Defects of Hydrothermal Niobium-doped KTiOPO_4

作　　者：覃世杰[1] 黄凌雄[2] 王金亮[1] 周海涛[1] 霍汉德[1] 张昌龙[1] 周卫宁[1] 

机构地区：[1]桂林矿产地质研究院,桂林541004 [2]中国科学院福州物质结构研究所,福州350002

出　　处：《人工晶体学报》2012年第6期1498-1501,1508,共5页Journal of Synthetic Crystals

基　　金：国家自然科学基金(60378032);国家高技术研究发展计划(863计划)(2006AA030110);中小企业创新基金(05C26224501278);广西青年科学基金(2010GXNSFB013011);广西科技攻关(0448084)

摘　　要：采用水热法在双温区加热炉中以Z-切向晶片为籽晶生长了掺铌KTiOPO4单晶(Nb∶KTP),得到尺寸为24.7mm×14.7 mm×42.6 mm的透明晶体。研究了Nb∶KTP水热条件下的生长习性和宏观、微观缺陷,通过其与纯KTP的透过谱的对比,对晶体质量进行了初步评估,与高质量的水热高抗灰迹KTP晶体有相当的质量。Single crystals of niobium-doped KTiOPO4（Nb∶ KTP） have been grown on Z-oriented seeds with a small addition of Nb2O5 using the hydrothermal technique out of a two zone furnace.Transparent crystals measuring up to 24.7 mm×14.7 mm×42.6 mm were obtained.The habit of the hydrothermal Nb∶ KTP was investigated.Macro-and micro-defects in Nb∶ KTP were also studied.Optical transmission spectra of Nb∶ KTP and pure KTP were measured for evaluating the quality of the Nb∶ KTP crystal.

关 键 词：水热法 掺铌KTP晶体 形貌 缺陷 

分 类 号：O713.5[理学—晶体学]