中温固体氧化物燃料电池NdBa_(0.5)Sr_(0.5)Co_2O_(5+δ)-GDC复合阴极材料的性能研究  

Performances of NdBa_(0.5)Sr_(0.5)Co_2O_(5+δ)-GDC as Potential Cathode Material for Intermediate-temperature Solid Oxide Fuel Cells

作　　者：孟祥伟[1] 吕世权[1] 李秀艳[1] 孙翠翠[1] 杨景海[1] 

机构地区：[1]吉林师范大学物理学院,吉林四平136000

出　　处：《吉林师范大学学报（自然科学版）》2013年第1期42-44,共3页Journal of Jilin Normal University:Natural Science Edition

基　　金：国家自然科学基金青年科学基金项目(10604020);吉林省教育厅"十一五"科学技术研究项目(20100145)

摘　　要：制备了复合阴极材料NdBa0.5Sr0.5Co2O5+δ-40%Ce0.9Gd0.1O1.95(NBSC-40%GDC).NBSC-40%GDC的平均热膨胀系数(TEC)为16.0×10-6K-1,其在700℃时极化电阻仅为0.134Ω.cm2.进行了以电解质为支撑体的单电池(NBSC-40%GDC/LSGM/NiO-GDC)的性能测试,在800℃时,功率密度达到382 mW.cm-2.Composite cathode material NdBa0.5 Sr0.5 Co2 O5＋δ-40% Ce0.9 Gd0.1 O1.95 （ NBSC-40% GDC ） was investigated. The average TEC values was 16.0 × 10 ^-6 K-1. The polarization resistance was as low as 0. 134 Ω · cm2 at 700 ℃. The electrolyte-supported fuel cell （NBSC-40% GDC/LSGM/NiO-GDC ） generated good performance with the maximum power density of 382 mW · cm-2 at 800 ℃.

关 键 词：阴极 固体氧化物燃料电池 电化学性能 

分 类 号：TM911.42[电气工程—电力电子与电力传动]