ZG20SiMn铸件的脆性断裂分析  

Brittle fracture analysis of ZG20SiMn cast

作　　者：宋勇 

机构地区：[1]大连华锐重工集团股份有限公司,辽宁大连116013

出　　处：《重型机械》2013年第1期91-93,共3页Heavy Machinery

摘　　要：针对某ZG20SiMn大型铸件开裂问题,通过对该铸件两种缺口与裂纹试样进行示波冲击试验和金相观察,分析了该铸件脆性断裂的原因是正火温度不够或保温时间不足,未能完全消除铸态组织,存在残余铸造内应力,并提出改进措施。The oscillographic impact test and metallographic observation for two types of the cast notches and cracks were made to solve the problem of cracks on a certain large-scale ZG20SiMn cast. It is found that the insufficiency of normalizing temperature or the shortage of temperature holding time is the reason of the brittle fracture of ZG20SiMn cast, in which the residual casting stress and the as-cast microstructure have not been completely eliminated. The improvement measures for such problems are also brought up in this paper.

关 键 词：脆性断裂分析 冲击韧性试验 魏氏组织 

分 类 号：TG222[金属学及工艺—铸造]