纳米TiO_2包覆磷酸钙生态防锈颜料的合成与性能  

Synthesis and Properties of Nano-TiO_2 Coated Calcium Phosphate Anticorrosive Pigment

作　　者：丁宇[1] 丁士文[1] 花东栓 李幕英 张宁[1] 

机构地区：[1]河北大学化学与环境科学学院,保定071002 [2]河北省水性涂料工程技术研究中心,徐水071002

出　　处：《科学技术与工程》2013年第3期783-785,共3页Science Technology and Engineering

基　　金：河北大学实验室开放基金(2010011);国家自然科学基金(20806018)资助

摘　　要：首先以工业85%磷酸,Ca(OH)2为基本原料合成磷酸钙中间体。再利用TiOSO4水解产生的TiO2对其包覆改性。经过滤、烘干得到产品。利用XRD、SEM对样品进行了表征。将改性的颜料制成醇酸水性防锈漆,喷涂到钢铁表面测试性能。结果证明,各项指标均达到或超过国家标准,尤其耐盐水一项,不仅优于目前市场上的磷酸锌,而且寿命比德国进口的ZPA防锈颜料要高出120 h。The calcium phosphate intermediate was firstly synthesized withindustrial phosphoric acid and Ca（OH）2 as the basic raw materials.Then,the final TiO2-coated calcium phosphate product was obtained by the hydrolysis of TiOSO4 after a filtration and drying process.The product was characterized by XRD,SEM,and EDS analysis.The as-obtained pigment was made into alkyd water-borne antirust coatings and painted on the surface of the steel to test its antirust performance.The results show that the as-synthesized product can meet or exceed the national standards.In particular,the salted water resistance properties of the product are not only superior to the commercial zinc phosphate pigment,but also exceed 120 h than German ZPA anticorrosive pigment

关 键 词：磷酸钙 纳米TiO2包覆 防锈颜料 水性涂料 

分 类 号：TQ628.3[化学工程—精细化工]