熔融碱法制备三重价态钙钛矿锰氧化物  

Preparation of Perovskite Manganites with Three Oxidation States via the Molten Hydroxide Method

作　　者：李明[1] 黄科科[1] 初学峰[1] 杜燕燕[1] 葛磊[1] 孙宇[1] 侯长民[1] 冯守华[1] 

机构地区：[1]无机合成与制备化学国家重点实验室,吉林大学化学学院,长春130012

出　　处：《高等学校化学学报》2013年第2期284-287,共4页Chemical Journal of Chinese Universities

基　　金：国家自然科学基金(批准号:90922034和21131002);高等学校博士学科点专项科研基金(批准号:20110061130005)资助

摘　　要：以MnO2,Ca(OH)2和La(OH)3为反应原料,在惰性气氛、低温(500℃)熔融KOH体系中合成了具有菱形钙钛矿结构Ca,K共掺杂的La0.64Ca0.25K0.11MnO3纳米材料,并对Mn的价态及磁学性能等进行了讨论.X射线光电子能谱(XPS)分析结果表明,La0.64Ca0.25K0.11MnO3纳米材料中的Mn具有三重混合价态,其零场冷却低温磁化率曲线表现出顺磁-铁磁转变,居里温度(Tc)为280 K.Ca-K codoped La0.64Ca0.25K0.11MnO3 nanocrystals with rhombohedral structure were synthesized in a molten KOH system at temperature as low as 500 ℃ in the atmosphere of Ar.The starting materials were MnO2,Ca（OH）2 and La（OH）3.Mn oxidation state and magnetic properties of La0.64Ca0.25K0.11MnO3 were discussed.XPS results demonstrate that there is a mixed valence of Mn in the nanocrystal.The zero-field-cooled（ZFC） curve indicates the samples undergo a paramagnetic（PM） to ferromagnetic（FM） phase transition and the Curie temperature（Tc） is 280 K.

关 键 词：熔融碱法 混合价态 钙钛矿 掺杂锰酸盐 

分 类 号：O611.4[理学—无机化学]