Crystallization Process of Polymorph A Enriched β-Zeolite

作　　者：童明全[1] 闫文付[1] 于吉红[1] 徐如人[1] 

机构地区：[1]吉林大学化学学院无机合成与制备化学国家重点实验室,长春130012

出　　处：《高等学校化学学报》2013年第3期494-498,共5页Chemical Journal of Chinese Universities

基　　金：国家自然科学基金(批准号:21171063);优秀青年科学基金(批准号:21222103);国家重点基础研究发展规划项目(批准号:2011CB808703)资助

摘　　要：以四乙基氢氧化铵(TEAOH)为结构导向剂,在超浓水热条件下合成了手性多形体A(简称A形体)过量的β沸石,对初始凝胶的性质及晶化过程进行了深入研究,测定了相应的晶化曲线.研究结果表明,与晶化出A形体含量低于50%的普通β沸石的合成体系相比,晶化出A形体过量的β沸石的合成体系中含水量极低,凝胶中过量的水必须在晶化之前通过加热去除,但过度去除初始凝胶中的水则会显著延长晶化时间.在晶化初期,产物中己出现A形体过量特征,随着晶化的进行,A形体的过量程度无显著变化.In the presence of tetraethylammonium hydroxide,the chiral polymorph A enriched β-zeolite was synthesized.The crystallization process of polymorph A enriched β-zeolite and the key factors that lead to the enrichment of polymorph A during crystallization were investigated.The results show that the enrichment of chiral polymorph A occurred in the early stage of crystallization and the degree of the enrichment of polymorph A did not change during the crystallization.