冠醚化合物对钢/铜和钢/铝摩擦副的抗磨减摩性能研究  

Anti-wear and Friction-reduction Properties of Crown Ether as Lubricating Additive for Steel/Copper and Steel/Aluminum

作　　者：夏延秋 刘维民[2] 张俊彦[2] 薛群基[2] 

机构地区：[1]沈阳工业大学机械学院,110023 [2]中国科学院兰州化学物理研究所固体润滑国家重点实验室,730000

出　　处：《润滑与密封》2000年第4期27-28,共2页Lubrication Engineering

基　　金：国家杰出青年基金!资助项目 编号 5 982 5 116

摘　　要：本文利用SRV摩擦磨损试验机研究了溴代苯并 - 15 -冠醚对钢 /铜、钢 /铝摩擦副的摩擦磨损性能的影响。结果表明 ,溴代苯并 - 15 -冠 - 5冠醚对钢 /铜摩擦副起到减摩抗磨作用 ,对钢 /铝摩擦副起到加速腐蚀磨损的作用。利用XPS对磨痕表面进行了分析 ,发现铜和铝磨痕上发现了Br,金属溴化物的生成减少了铜的摩擦和磨损 ,但却由于腐蚀而加速了铝合金的磨损。The anti-wear and friction-reduction of brominobenzene-15-crown as additive in base oil were evaluated on an Optimol SRV friction and wear tester with steel/copper and steel /aluminum pairsThe result show that brominobenzene-15-crown-5 decreases wear and friction for copper alloy,but increases wear of aluminumThe Br was detected in the worn surface with X-ray photoelctron spectroscopy (XPS),It is suggested that bromide decrease friction and wear of copper ,but increase wear of aluminum

关 键 词：钢/铝 钢/铜 减摩抗磨性能 冠醚化合物 

分 类 号：TH117.22[机械工程—机械设计及理论]