添加LiFe_5O_8对NiZn铁氧体材料性能的影响  

Effect of LiFe_5O_8 dopant on the properties of NiZn ferrite material

作　　者：孙蒋平 聂敏[1] 徐方舟[1] 申志刚[1] 

机构地区：[1]天通控股股份有限公司磁性材料事业本部,浙江海宁314400

出　　处：《磁性材料及器件》2013年第1期44-46,55,共4页Journal of Magnetic Materials and Devices

摘　　要：采用传统氧化物法制备NiZn铁氧体材料,考察了添加锂铁氧体LiFe5O8对NiZn铁氧体材料电磁性能的影响。实验表明,添加少量LiFe5O8可以提高NiZn铁氧体材料的烧结密度、起始磁导率和品质因数Q,但是过高的烧结温度会造成材料的晶粒过度生长,从而Q值下降;当LiFe5O8的添加量为5wt%、烧结温度为1060℃时,制备的材料具有较高的起始磁导率和Q值。Conventional oxide ceramic method was used to prepare NiZn ferrites, and effect of LiFe8O8 dopant on their magnetic properties was studied. The experimental results showed that a small amount of LiFe8O8 dopant improves the sintering density, initial permeability and the quality factor Q of the prepared material, but too high sintering temperature results in excessive grain growth and the Q value is deteriorated. The prepared material with anamount of LiF5O8 dopant of 5wt% has relatively high initial permeability and high Q value.

关 键 词：NIZN铁氧体材料 LiFe5O8添加 磁性能 