高性能水性木器漆用PUA树脂的制备及漆膜性能研究  

Preparation of Polyurethane-Acrylate(PUA) Resins for High Performance Waterborne Wood Coating and Its Film Properties

作　　者：乔永洛[1] 舒金兵[1] 申亮[1] 

机构地区：[1]江西科技师范大学有机功能分子研究所,南昌330013

出　　处：《涂料工业》2013年第4期30-36,共7页Paint & Coatings Industry

基　　金：国家自然科学基金项目(51063002);江西省教育厅青年科学基金项目(GJJ09571)

摘　　要：以水性PU乳液为原料,通过与丙烯酸酯单体共聚制备了稳定的PUA复合乳液。重点考察了PU的加料方式、PU用量以及丙烯酸酯单体的配比对聚合过程和乳液性能的影响。研究表明,在种子乳液聚合基础上采用核壳两层预乳化工艺,PU用量为20%,丙烯酸酯单体配比m(MMA)∶m(BA)∶m(2-EHA)=6∶2∶2时可得到性能优异的PUA复合乳液。漆膜性能的测试结果表明,该PUA乳液配制的水性木器清漆具有优异的性能,可满足高档木器对漆膜的高性能要求。A polyurethane- acrylates（PUA） composite emulsion was prepared by copoly- merization of acrylate monomer and aqueous polyurethane dispersions （PUD）. The effects of the feeding methods, amount of PUD and the composition of acrylate monomers on both poly- merization process and the performances of the composite emulsion were mainly discussed. The results showed that the PUA emulsion with excellent comprehensive performance could be ob- tained by using core - shell pre - emulsification technology when the percent of PU was 20% and the composition of acrylate monomers was m （ MMA ） ： m （ BA ） ： m （ 2 - EHA ） = 6 ： 2 ： 2. The test results of all kinds of properties of PUA coating film indicated that the waterborne wood varnish prepared with the above PUA composite emulsion showed excellent performance, and it can meet the high requirements of high- grade woodenwares.

关 键 词：PUA复合乳液 高性能 木器涂料 

分 类 号：TQ635.3[化学工程—精细化工]