超临界流体制备纳米Al_2O_3/镍基复合电铸层及其微观结构和显微硬度  

Preparation of Ni-Based Composite Electroforming Layer with Nano-Al_2O_3 Particles by Supercritical Fluids and Its Microstructure and Microhardness

作　　者：姜博[1,2] 雷卫宁[1,2] 刘维桥[1] 钱蜜[2] 

机构地区：[1]江苏理工学院机械工程学院,常州213001 [2]常州大学机械工程学院,常州213016

出　　处：《机械工程材料》2013年第3期58-60,79,共4页Materials For Mechanical Engineering

基　　金：国家自然科学基金资助项目(50875116);江苏省自然科学基金资助项目(BK2012585)

摘　　要：在超临界流体条件下制备了纳米Al2O3/镍基复合电铸层,采用显微硬度仪和扫描电镜分析了复合电铸层的微观结构和显微硬度。结果表明:在超临界流体条件下进行电铸,可有效解决Al2O3纳米颗粒在镀液中的团聚问题,并促进其在电铸层中均匀弥散分布;随Al2O3添加量的增多,电铸层的显微硬度先升后降;在超临界流体压力为14MPa、镀液中Al2O3添加量为60g.L-1时,电铸层的显微硬度最大,为1 142.2HV,此时电铸层中Al2O3的质量分数为9.88%。Ni-based composite electroforming layer with nano-A12O3 pairticles was prepared under the condition of supercritical fluid, and microstructure and mierohardness were analysed by micro hardness tester and scanning electron microscopy. The results show that aggregation problem of nano-A12 O3 particles was resolved effectively by electroforming under the condition of supercritical fluid, and electroforming made nano-A12 O3 particles distribute in electroforming layer evenly. The microhardness of electroforming layer increased and then decreased with the increase of adding amounts of A12O3 particles. Microhardness of the electroforming layer up to maximum （1 142.2 HV） and mass fraction of A12 O3 in electroforming layer was 9.88% when pressure of the supercritical fluid was 14 MPa and adding amount of A12 03 particles in plating solution was 60 g · L 1.

关 键 词：超临界流体 Al2O3纳米颗粒 镍基复合电铸层 

分 类 号：TG153.2[金属学及工艺—热处理]