SYNTHESIS AND CHARACTERIZATION OF BIODEGRADABLE POLYESTERAMIDES CONSTRUCTED MAINLY BY ALTERNATING DIESTERDIAMIDE UNITS FROM N,N'-BIS(2-HYDROXYETHYL)-ADIPAMIDE AND DIACIDS  

作　　者：Hui-yun Sun Tiao Yin 赵京波 Zhi-yuan Zhang Wan-tai Yang 

机构地区：[1]Key Laboratory of Carbon Fiber and Functional Polymers,Ministry of Education [2]State Key Laboratory of Chemical Resource Engineering,College of Materials Science and Engineering,Beijing University of Chemical Technology

出　　处：《Chinese Journal of Polymer Science》2013年第3期452-461,共10页高分子科学（英文版）

基　　金：financially supported by the National Natural Science Foundation of China (Nos.50873013 and 21244006)

摘　　要：Two kinds of aliphatic alternating polyesteramide prepolymers were prepared through melt polycondensation from N,N＇-bis（2-hydroxyethyl）-adipamide and adipic acid or sebacic acid. Chain extension of them was conducted with 2,2＇-（1,4- phenylene）-bis（2-oxazoline） and adipoyl biscaprolactamate as combined chain extenders. The chain extended polyesteramides （ExtPEAs） were characterized by IR, 1H-NMR, differential scanning calorimetry, thermogravimetric analysis, wide angle X-ray scattering, tensile test and enzymatic degradation. The results showed that the ExtPEA（4,m）s were mainly constituted with the diester adipamide alternating units. ExtPEA（4,4） and ExtPEA（4,8） had Tm of 83.8℃ and 85.8℃ and initial decomposition temperature above 310.0℃. They crystallized similarly as Nylon-66 did and were flexible thermoplastic materials with tensile strength up to 25.64 MPa and strain at break up to 737%.Two kinds of aliphatic alternating polyesteramide prepolymers were prepared through melt polycondensation from N,N＇-bis（2-hydroxyethyl）-adipamide and adipic acid or sebacic acid. Chain extension of them was conducted with 2,2＇-（1,4- phenylene）-bis（2-oxazoline） and adipoyl biscaprolactamate as combined chain extenders. The chain extended polyesteramides （ExtPEAs） were characterized by IR, 1H-NMR, differential scanning calorimetry, thermogravimetric analysis, wide angle X-ray scattering, tensile test and enzymatic degradation. The results showed that the ExtPEA（4,m）s were mainly constituted with the diester adipamide alternating units. ExtPEA（4,4） and ExtPEA（4,8） had Tm of 83.8℃ and 85.8℃ and initial decomposition temperature above 310.0℃. They crystallized similarly as Nylon-66 did and were flexible thermoplastic materials with tensile strength up to 25.64 MPa and strain at break up to 737%.

关 键 词：Alternating polyesteramides POLYCONDENSATION Chain extension Diamidediol Properties. 

分 类 号：O631.3[理学—高分子化学]