Magnetic properties and magnetostriction of PrxNd_(1-x)Fe_(1.9)(0≤x≤1.0) alloys at low temperature  

作　　者：王永 唐少龙 李玉龙 谢忍 都有为 

机构地区：[1]Nanjing National Laboratory of Microstructures,Jiangsu Provincial Laboratory for Nanotechnology,and Department of Physics, Nanjing University

出　　处：《Chinese Physics B》2013年第3期487-490,共4页中国物理B（英文版）

基　　金：Project supported by the National Basic Research Program of China (Grant No. 2012CB932304);the National Natural Science Foundation of China (Grant Nos. 50831006 and 50771055);the Priority Academic Program Development of Jiangsu Higher Education Institutions,China

摘　　要：The crystal structure,magnetic and magnetostrictive properties of high-pressure synthesized Prx Nd1-xFe1.9（0≤x≤1.0） alloys were studied.The alloys exhibit single cubic Laves phase with MgCu 2-type structure.The initial magnetization curve reveals that Pr0.2Nd0.8Fe1.9 has a minimum magnetocrystalline anisotropy at 5 K.The magnetostriction curve at 5 K shows that Pr0.2Nd0.8Fe1.9 has a very good low-field magnetostrictive property,and the magnetostriction of the PrxNd1-xFe1.9 alloy in high magnetic field is attributable mainly to Pr.The temperature dependence of the magnetostriction（λ ｜｜） at the field of 5 kOe shows that the substitution of Nd reduces the K 1 remarkably,and the values of λ｜｜ of Pr0.2Nd0.8Fe1.9 and Pr0.8Nd0.2Fe1.9 alloys are nearly five times larger than that of the PrFe 1.9 alloy below 50 K;the λ｜｜ of Pr0.8Nd0.2Fe1.9 reaches up to 1082 ppm at 100 K,which makes it a potential candidate for application in this temperature range.The crystal structure,magnetic and magnetostrictive properties of high-pressure synthesized Prx Nd1-xFe1.9（0≤x≤1.0） alloys were studied.The alloys exhibit single cubic Laves phase with MgCu 2-type structure.The initial magnetization curve reveals that Pr0.2Nd0.8Fe1.9 has a minimum magnetocrystalline anisotropy at 5 K.The magnetostriction curve at 5 K shows that Pr0.2Nd0.8Fe1.9 has a very good low-field magnetostrictive property,and the magnetostriction of the PrxNd1-xFe1.9 alloy in high magnetic field is attributable mainly to Pr.The temperature dependence of the magnetostriction（λ ｜｜） at the field of 5 kOe shows that the substitution of Nd reduces the K 1 remarkably,and the values of λ｜｜ of Pr0.2Nd0.8Fe1.9 and Pr0.8Nd0.2Fe1.9 alloys are nearly five times larger than that of the PrFe 1.9 alloy below 50 K;the λ｜｜ of Pr0.8Nd0.2Fe1.9 reaches up to 1082 ppm at 100 K,which makes it a potential candidate for application in this temperature range.

关 键 词：MAGNETOSTRICTION rare-earth compounds cubic Laves phase high-pressure annealing 

分 类 号：TG132.2[一般工业技术—材料科学与工程]