ZrB_2对Al_2O_3-ZrB_2-SiC复相陶瓷室温力学性能影响  

Effects of ZrB_2 on Mechanical Properties of Al_2O_3-ZrB_2-SiC Composite Ceramics at Room Temperature

作　　者：徐广平 何江荣 魏赛[2] 冯伟[2] 谢志鹏[2] 

机构地区：[1]东台市节能耐火材料厂,江苏东台2242132 [2]清华大学材料科学与工程系,北京100084

出　　处：《中国陶瓷工业》2013年第1期22-24,共3页China Ceramic Industry

摘　　要：Al2O3陶瓷具有优异的室温和高温性能,但其脆性大,断裂韧性较低,限制了其应用。采用热压烧结工艺制备了应用于不同环境的Al2O3-ZrB2-SiC复相陶瓷(简称AZS),主要研究不同含量的ZrB2对Al2O3-SiC基陶瓷性能的影响。力学性能研究发现,当Al2O3陶瓷中ZrB2和SiC的体积百分比分别为20%和5%时,AZS3陶瓷具有最高的强度和韧性,分别为508.5MPa和6.65MPa.m1/2,相比纯氧化铝陶瓷的468.6MPa和5.56 MPa.m1/2提高了8.5%和19.6%。Al2O3ceramics has excellent performance both at room temperature and high temperature, but its brittleness and low fracture toughness limit certain applications at high temperatures. Al2O3-ZrB2-SiC composite ceramics （AZS） used in high temperature environment were prepared by hot pressing sintering process, the influence of ZrB2 content on Al2O3-SiC performance was investigated. The results showed that with 20 vol% ZrB2 and 5 vol% SiC, AZS ceramic has the highest strength and toughness, as 508.5MPa and 6.65MPa.m^1/2, respectively. Compared to pure alumina ceramic （468.60MPa and 5.56 MPa.m^1/2）, its properties increased 8.5% and 19.6%, respectively.

关 键 词：Al2O3-ZrB2-SiC 复相陶瓷 力学性能 

分 类 号：TQ174.1[化学工程—陶瓷工业]