CPE用HDPE粉料树脂的开发  

Development of HDPE powder resin for CPE

作　　者：王景良[1] 张希来[1] 陈雷[1] 韩云艳[1] 王黎国[2] 

机构地区：[1]中国石油天然气股份有限公司大庆石化分公司塑料厂,黑龙江省大庆市163714 [2]中国石油天然气股份有限公司大庆物业中心,黑龙江省大庆市163714

出　　处：《合成树脂及塑料》2013年第2期51-53,共3页China Synthetic Resin and Plastics

摘　　要：在高密度聚乙烯(HDPE)装置上采用於浆法工艺开发生产了氯化聚乙烯用的HDPE粉料树脂QL505P。QL505P的熔体流动速率为0.3～0.6 g/10 min,密度为0.953～0.958 g/cm3,熔流比为7～16,粉料堆密度大于或等于0.36 g/cm3。产品生产过程稳定,可满足用户要求。High density polyethylene （HDPE） powder resin QL505P for chlorinated polyethylene was produced in a HDPE plant with slurry process. The product had melt flow rate of 0.3-0.6 g / 10 rain, density of 0.953-0.958 g/cm^3, melt flow rate ratio of 7-16 and powder bulk density equal to or more than 0.36 g/cm^3. The production process was stable and the product could meet the requirements of customers.

关 键 词：高密度聚乙烯 氯化聚乙烯 粉料 

分 类 号：TQ325.12[化学工程—合成树脂塑料工业]