Tribological Properties of MAO Coating with Nano-graphite on ZM5 Magnesium Alloy

作　　者：杨志成[1] 吴向清[1] 谢发勤[1] 姚小飞[1] 

机构地区：[1]西北工业大学航空学院,西安710072

出　　处：《中国表面工程》2013年第2期45-50,共6页China Surface Engineering

基　　金：国家基础研究发展计划(973计划)(2007CB607603)

摘　　要：添加纳米石墨颗粒的硅酸盐溶液中制备ZM5合金微弧氧化陶瓷层,利用SEM、EDS和XRD分析了涂层的微观形貌、成分及物相组成,用球-盘干磨损试验对涂层的室温摩擦磨损行为进行研究。结果表明,纳米石墨改性微弧氧化陶瓷层主要由Mg2SiO4、少量的MgO、Mg和C相组成,石墨以机械形式分散于陶瓷层中并起到减摩作用。4.9N载荷下体积磨损率为9.19×10-5 mm3/Nm,是无石墨微弧氧化陶瓷层的1/3,ZM5基体的1/14;9.8N载荷下体积磨损率为1.44×10-4 mm3/Nm,是无石墨微弧氧化陶瓷层的2/5,ZM5基体的1/8,与无石墨微弧氧化陶瓷层相比显著提高了镁合金基体的耐磨性,且其室温干摩擦磨损机理为疲劳磨损,磨痕呈疲劳剥落形貌。Micro-arc oxidation（MAO） ceramic coating of ZM5 alloy was prepared in the silicate electrolyte system with nano-graphite particle. The micro morphology, chemical and phase composition were investigated by SEM, EDS and XRD. At room temperature, the tribological properties of coatings were evaluated by a ball -on-disc wear test machine. The results show that the MAO ceramic coating with nano-graphite is composed by Mg2SiO4 , MgO, Mg, and C. Graphite disperses in the coating through mechanical effect and shows anti- friction effect. The volume friction rate of the MAO ceramic coating with nano-graphite is 9.19×10^-2 mma/Nm under the load of 4.9 N. It is one-fourteenth of that of ZM5 substrate and one-third of that of MAO ceramic coating without graphite. The volume friction rate of the MAO ceramic coating with nano-graphite is 1.44~ 10-4 mma/Nm under the load of 9.8 N. It is one-eighth of that of ZM5 substrate and two-fifth of that of the MAO ceramic coating without graphite. The wear resistance of ZM5 substrate increases dramatically because of the MAO ceramic coating with nano-graphite. The wear mechanism of the MAO ceramic coating with nano -graphite is fatigue wear from the fatigue spalling morphology.

关 键 词：ZM5合金 微弧氧化 纳米石墨 摩擦磨损性能 

分 类 号：TG174.45[金属学及工艺—金属表面处理] TG115.58[金属学及工艺—金属学]