特种车辆用聚氨酯导热绝缘密封胶的研制  

Polyurethane Sealant with Insulation Thermal Conductivity for Special Vehicle

作　　者：庞金录[1] 唐功庆[2,3] 张梅[2,3] 姜志国[2,3] 王丛[1] 

机构地区：[1]北京北方车辆集团有限公司,北京100072 [2]北京化工大学材料科学与工程学院,北京100029 [3]北京市新型高分子材料制备与加工重点实验室,北京100029

出　　处：《聚氨酯工业》2013年第2期30-33,共4页Polyurethane Industry

摘　　要：以聚醚多元醇和甲苯二异氰酸酯为主要原料、硅烷偶联剂改性氮化铝(AlN)为填料制备了适用于特种车辆中央处理器的电源密封的聚氨酯导热绝缘密封胶,讨论了AlN的平均粒径和用量对该密封胶导热系数、绝缘性能以及力学性能的影响。结果表明,纳米级改性AlN在明显改善密封胶导热性的同时,可以保持材料优异的力学性能;当改性AlN质量分数达到48%时,聚氨酯导热绝缘密封胶的导热系数达到0.453 W/(m.K),表面电阻为1.5×109Ω,体积电阻为2.6×1010Ω,拉伸强度达到0.9 MPa,满足特种车辆中央处理器的电源密封要求。With polyether polyol and toluene diisocynate as the main materials and modified aluminum nitride （AlN） as filler, the thermally conductive and electrically insulating polyurethane sealant which was used for special vehicle central centroller was produced. The effect of the average diameter size and the content of modified AlN on the thermal conductivity, insulating and mechanical properties of sealant was discussed. The result showed that modified AlN not only improved the thermal conductivity of sealant but also maintained the satisfying mechanical properties. When the mass content of modified AlN was 48% , the thermal conductivity of polyurethane sealant was 0. 453 W/（m-K） , the surface resistance was 1.5 × 10^9 Ω, the volume resistance was 2. 6× 10^10Ω, with the tensile strength 0.9 MPa. This sealant could fit the central controller of special vehicles demand.

关 键 词：聚氨酯 密封胶 导热 绝缘 氮化铝 

分 类 号：TQ436.6[化学工程]