预腐蚀LY12CZ铝合金疲劳裂纹扩展行为研究  

Research on Fatigue Cracking Behavior of LY12CZ Aluminum Alloy with Corrosion Damage

作　　者：李旭东[1] 王玉刚[1] 苏维国[1] 丁文勇[1] 

机构地区：[1]海军航空工程学院青岛校区,山东青岛266041

出　　处：《青岛科技大学学报（自然科学版）》2013年第2期182-187,共6页Journal of Qingdao University of Science and Technology:Natural Science Edition

摘　　要：腐蚀疲劳是一种在机械应力和腐蚀介质联合作用下的材料退化行为。这种材料退化对于航空工业是一个严峻的问题。因此利用扫描电镜原位技术对于预腐蚀LY12CZ铝合金进行了实验研究。实验结果表明腐蚀损伤对于铝合金疲劳裂纹扩展行为具有强烈的影响,这种影响可以用腐蚀坑深度来表征。并提出了一种评价铝合金腐蚀疲劳裂纹行为的方法。Corrosion fatigue is a form of degradation subjected to combined damage of mechanical stress and corrosive medium, which is a severe issue in aircraft industry. Ex- perimental investigations on prior corrosion fatigue cracking behavior of LY12CZ were conducted with scanning electron microscope （SEM）. Results indicate corrosion damage is important for the fatigue cracking behavior of LY12CZ aluminum alloy. The effect of corrosion pit on fatigue crack can be characterized by the depth of corrosion pit. A meth- od to evaluate corrosion fatigue crack growth for AA LY12CZ is proposed.

关 键 词：疲劳裂纹 铝合金 预腐蚀 微结构 SEM原位技术 

分 类 号：TG171[金属学及工艺—金属表面处理] V252[金属学及工艺—金属学]