热轧工艺对AZ31B镁合金薄板组织及性能的影响  

Effect of hot-rolling technology on microstructure and mechanical properties of AZ31B magnesium alloy sheet

作　　者：李宏战[1] 李争显[1] 杜继红[1] 赵永庆[1] 高广睿[1] 王培[1] 杨海彧[1] 

机构地区：[1]西北有色金属研究院,陕西西安710016

出　　处：《轻合金加工技术》2013年第6期38-42,共5页Light Alloy Fabrication Technology

摘　　要：研究了经不同温度(400℃、450℃)和道次变形量(10%、15%、20%)热轧的AZ31B镁合金薄板显微组织及不同方向的力学性能。结果表明,AZ31B镁合金经过热轧后,组织得到明显细化,力学性能得到大幅度提高。在450℃热轧,当道次压下量从10%增加到20%时,抗拉强度从334 N/mm2增加到344 N/mm2,屈服强度由263 N/mm2提高到284 N/mm2,伸长率则由12.5%升高到15%。热轧镁合金薄板形成以{0002}基面为主的平行于板面的强织构,使得其各向异性增强。The microstructure and mechanical properties at different planar directions of AZ31B magnesium alloy sheet being hot-rolled at different temperature （400℃ ,450℃ ） and different pass reduction rate （ 10%, 15%, 20% ） have been investigated. The results show that after hot-rolling, the microstructure of AZ31 B magnesium alloy has been refined and me- chanical properties have been increased greatly ;the tensile strength has been increased from 334 N/mm2 to 344 N/mm2, the yield strength has been increased from 263 N/mm2 to 284 N/ mm and the elongation has been increased from 12.5% to 15% while pass reduction being increased from 10% to 20% at 450℃hot rolling. The anisotropy has been increased due to the {00021 major texture forming as the basal plane which parallel along the rolling surface of the hot-rolled AZ31B magnesium alloy sheet.

关 键 词：AZ31B镁合金 热轧工艺 组织 性能 

分 类 号：TG146.22[一般工业技术—材料科学与工程] TG339[金属学及工艺—金属材料]