环氧硅油改性乙烯基/氨基硅油的制备及应用性能  

Synthesis and application performance of epoxy silicone modified vinyl/amino containing silicone

作　　者：雷宁[1] 安秋凤[1] 肖波[1] 

机构地区：[1]陕西科技大学教育部轻化工助剂化学与技术重点实验室,陕西西安710021

出　　处：《印染助剂》2013年第6期9-11,14,共4页Textile Auxiliaries

基　　金：教育部博士点基金项目(200807080002);陕西省教育厅重点项目(09JS060)

摘　　要：以乙烯基/氨基硅油(Vi-ASO-1)和环氧硅油(ESO)为原料,合成了无色微透明的环氧硅油改性乙烯基/氨基硅油(Vi-EASO-1),并通过IR对其结构进行了表征.Vi-EASO-1经乳化后得到的乳液Z-均平均粒径为52.73 nm,Zeta电位值为+32.2 mV.Vi-EASO-1乳液整理的涤纶织物具有良好的防水性,其静态接触角可以达到141°.A colorless and slightly transparent epoxy silicone modified vinyl/amino containing silicone （Vi-EASO-1） was synthesized using vinyl/amino containing silicone （Vi-ASO-1） and epoxy silicone （ESO） as raw materials, and its structure was characterized by IR. The average Z-particle size of emulsified Vi-EASO-1 emulsion was 52.73 nm, and Zeta potential value was ＋32.2 mV. Polyester fabric finished by Vi-EASO-1 emul- sion had good waterproofing property with 141°of static contact angle.

关 键 词：环氧硅油改性乙烯基 氨基硅油 涤纶织物 防水性 

分 类 号：TQ219[化学工程—有机化工] TQ264.17