TiO_2/ZnO纳米复合材料的制备及表征  

Preparation and characterization of TiO_2/ZnO nanocomposites

作　　者：陶玉贵[1] 曹宁[1] 宋旸[1] 孙忆晨[1] 金成[1] 

机构地区：[1]安徽工程大学生物与化学工程学院,芜湖241000

出　　处：《化工新型材料》2013年第6期112-114,共3页New Chemical Materials

基　　金：安徽省自然科学基金(1308085MC51);安徽省高校自然科学基金重点项目(KJ2012A034)

摘　　要：以钛酸正四丁酯及L-Cys为钛源和模板剂仿生合成纳米TiO2前体,采用水热合成法制备TiO2/ZnO纳米复合材料,并利用XRD、SEM、XPS、FT-IR以及比表面积及孔径分析等对TiO2/ZnO纳米复合材料进行表征。结果表明:合成TiO2/ZnO复合材料是由锐钛矿TiO2和纤锌矿ZnO组成,形貌是由许多几十纳米厚薄片组成的花状,直径在2～3μm之间,比表面积为219.54m2/g。TiO2/ZnO nanocomposites were synthesized through a facile hydrothermal method using Zn（N（）a ）z ＊ 6Hz O and nano TiO2 precursors which were repared through biomimetic method. The samples were characterized by XRD, SEM, XPS, FT-IR and N2 adsorption-desorption experiments. The results showed that nanocomposites were combination of anatase TiO2 and wurtzite ZnO, about 2 3/,m in diameter, flower-like morphology consisting of many tens of nanometers thick slices and the specific surface area up to 219.54m2g 1.

关 键 词：TIO2 ZNO 纳米复合材料 表征 

分 类 号：TB383.1[一般工业技术—材料科学与工程] O614.411[理学—无机化学] TB33[理学—化学]